| Property | Value |
|---|---|
| Mechanical Properties | |
| Ultimate tensile strength | 30 – 59 MPa |
| Yield strength | 9 MPa |
| Young’s modulus (modulus of elasticity) | 2.9 – 3.1 GPa |
| Elongation at break | 330 – 587 % |
| Hardness | 85A – 95A |
Skip to content Plastic
FDM
| Property | Value |
|---|---|
| Mechanical Properties | |
| Ultimate tensile strength | 30 – 59 MPa |
| Yield strength | 9 MPa |
| Young’s modulus (modulus of elasticity) | 2.9 – 3.1 GPa |
| Elongation at break | 330 – 587 % |
| Hardness | 85A – 95A |
Aluminum, Alloy Steel
± 0.3% starting from ± 0.3 mm
(0.012 in)
Lead duration: 5 business days
Laser Cutting. Bending, Post-Processing
Tolerances as low as ± 0.04 in (0.1 mm)
Lead duration: 5 business days
Prototypes and production tooling
Wide range of part complexities and sizes
1 to 1M parts
Milling, turning and post-processing
Tolerances down to ±.020 mm (±.001 in)
Lead times from 5 business days
FDM, SLA, SLS, MJF
± 0.3% with a lower limit of ± 0.3 mm (± 0.012 in)
Lead times from 1 business day
Friction Stir Welding: A Solid-State Metal Joining Process It is applied for using as a solid state welding
New volumetric additive techniques are overcoming traditional 3D printing’s layer-by-layer constraints. By projecting patterns into specially formulated resins,
Cold spray coating technology refers to a coating technique whereby metallic powder particles are held in position within
The table of contents for the exploration of acoustic 3D printing includes several key sections. It begins with
3D printing technology has rapidly evolved in recent years which allowed manufacturers to deposit materials to form objects
The 3D printing plastics market is experiencing significant growth, driven by advancements in technology and increasing demand across
Copyright © 2025 MXY Machining
Copyright © 2025 MXY Machining
English 
Français 
Deutsch (Sie) 
Español 
Bahasa Indonesia 
Italiano 
日本語 
한국어 
Nederlands (Formeel) 
Português do Brasil 
Русский 
Türkçe 
简体中文