Stainless steel 15-5 | 1.4545 | X5CrNiCu15-5
Property Value Mechanical Properties Ultimate tensile strength 890 – 1200 MPa Yield strength 590 – 890 MPa Young’s modulus (modulus of elasticity) 190 – 196 GPa Elongation at break 7 – 16 % Physical Properties Corrosion resistance Good Magnetism Magnetic Weldability Good Thermal Properties Maximum service temperature 820 °C Thermal expansion coefficient 10.4 – 11.7 […]
Stainless steel 301 | 1.4310 | X10CrNi18-8
Property Value Mechanical Properties Ultimate tensile strength 510 – 590 MPa Yield strength 200 – 230 MPa Young’s modulus (modulus of elasticity) 200 – 212 GPa Elongation at break 35 – 46 % Physical Properties Corrosion resistance Excellent Magnetism Non-magnetic in annealed condition Weldability Good Thermal Properties Thermal expansion coefficient 16.6 – 19.5 × 10-6/ºC […]
Stainless steel 430 | 1.4016 | X6Cr17
Property Value Mechanical Properties Ultimate tensile strength 450 – 500 MPa Yield strength 200 – 280 MPa Young’s modulus (modulus of elasticity) 200 GPa Elongation at break 20 – 24 % Physical Properties Corrosion resistance Good Magnetism Magnetic Weldability Good Thermal Properties Maximum service temperature 815 – 870 °C Thermal expansion coefficient 10.4 – 11.3 […]
Stainless steel 440C | 1.4125 | X105CrMo17
Property Value Mechanical Properties Ultimate tensile strength 560 – 800 MPa Yield strength 340 – 430 MPa Young’s modulus (modulus of elasticity) 204 – 215 GPa Elongation at break 14 – 18 % Physical Properties Corrosion resistance Moderate Magnetism Magnetic Weldability Poor Thermal Properties Thermal expansion coefficient 10 – 10.2 × 10-6/ºC Thermal conductivity 22 […]
Stainless steel 420 | 1.4028 | X30Cr13
Property Value Mechanical Properties Ultimate tensile strength 485 – 750 MPa Yield strength 275 – 380 MPa Young’s modulus (modulus of elasticity) 190 – 205 GPa Elongation at break 15 – 20 % Physical Properties Corrosion resistance Moderate Magnetism Magnetic UV resistance Excellent Weldability Good Thermal Properties Maximum service temperature 144 – 194 °C Thermal […]
Stainless steel 2205 Duplex | 1.4462 | 2205 | X2CrNiMoN 22-5-3
Property Value Mechanical Properties Ultimate tensile strength 620 – 700 MPa Yield strength 425 – 500 MPa Young’s modulus (modulus of elasticity) 195 – 205 GPa Elongation at break 14 – 28 % Physical Properties Corrosion resistance Excellent Magnetism Magnetic UV resistance Excellent Weldability Good Thermal Properties Maximum service temperature 335 – 365 °C Thermal […]
Stainless steel 416 | 1.4005 | X12CrS13
Stainless steel 303 | 1.4305 | X8CrNiS18-9
Property Value Mechanical Properties Ultimate tensile strength 580 – 700 MPa Yield strength 205 – 350 MPa Young’s modulus (modulus of elasticity) 192 – 200 GPa Elongation at break 40 – 50 % Physical Properties Corrosion resistance Moderate Magnetism Non-magnetic UV resistance Excellent Weldability Very Poor Thermal Properties Maximum service temperature 750 – 925 °C […]
Stainless Steel 17-4 PH | 1.4542 | X5CrNiCuNb16-4 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 790 – 1200 MPa Yield strength 520 – 860 MPa Young’s modulus (modulus of elasticity) 197 – 207 GPa Elongation at break 3 – 16 % Physical Properties Corrosion resistance Excellent Magnetism Magnetic UV resistance Excellent Weldability Moderate Thermal Properties Maximum service temperature 282 – 316 °C Thermal […]
Stainless steel 316/316L | 1.4401/1.4404 | X5CrNiMo17-12-2/X2CrNiMo17-12-2
Property Value Mechanical Properties Ultimate tensile strength 480 – 600 MPa Yield strength 170 – 230 MPa Young’s modulus (modulus of elasticity) 190 – 205 GPa Elongation at break 38 – 55 % Physical Properties Corrosion resistance Excellent Magnetism Non-magnetic UV resistance Excellent Weldability Excellent Thermal Properties Maximum service temperature 750 – 925 °C Thermal […]