ABS
Definition of CNC Machined ABS Parts ABS, which stands for (Acrylonitrile Butadiene Styrene), is a widely used thermoplastic polymer made by combining acrylonitrile, butadiene, and styrene. This material blends the strength and heat resistance of acrylonitrile, the toughness of butadiene rubber, and the stiffness and ease of manufacturing of styrene. ABS is known for being lightweight, strong, […]
Tool steel H13 | 1.2344 | X40CrMoV5-1 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 690 MPa Yield strength 330 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Thermal expansion coefficient 10.4 – 12.4 × 10-6/ºC Thermal conductivity 22 – 29 W/(m⋅°C) Electrical Properties Electrical resistivity 52 – 86 μΩ*cm […]
Tool steel S7 | 1.2355 | 50CrMoV13-15 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 640 – 670 MPa Yield strength 370 – 380 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 – 25 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Maximum service temperature 165 – 215 °C Thermal expansion coefficient 10.7 – 11.2 × 10-6/ºC Thermal […]
Tool steel A3 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 700 MPa Yield strength 340 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 % Physical Properties Corrosion resistance Poor Magnetism Magnetic Weldability Poor Thermal Properties Thermal expansion coefficient 11.8 – 14.3 × 10-6/ºC Thermal conductivity 37 W/(m⋅°C) Post Treatments Post-Processing Cold work, Annealing, Quenching, […]
Tool steel O1 | 1.2510 | 100MnCrW4 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 640 – 720 MPa Yield strength 400 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 20 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Maximum service temperature 165 – 215 °C Thermal expansion coefficient 11.3 – 11.8 × 10-6/ºC Thermal conductivity 41.2 – 44.6 […]
Tool steel A2 | 1.2363 | X100CrMoV5-1- Annealed state
Property Value Mechanical Properties Ultimate tensile strength 670 – 710 MPa Yield strength 345 – 350 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 21 % Physical Properties Magnetism Magnetic Weldability Moderate Thermal Properties Maximum service temperature 195 – 245 °C Thermal expansion coefficient 10.5 – 11 × 10-6/ºC Thermal conductivity 36.1 […]
Tool steel D2 | 1.2379 | X153CrMoV12-1 – Annealed state
Property Value Mechanical Properties Ultimate tensile strength 758 – 860 MPa Yield strength 420 – 470 MPa Young’s modulus (modulus of elasticity) 190 GPa Elongation at break 16 % Physical Properties Magnetism Magnetic Weldability Poor Thermal Properties Maximum service temperature 195 – 245 °C Thermal expansion coefficient 10.3 – 12 × 10-6/ºC Thermal conductivity 29.3 […]
Titanium Grade 1 | 3.7025
Property Value Mechanical Properties Ultimate tensile strength 310 – 350 MPa Yield strength 220 – 240 MPa Young’s modulus (modulus of elasticity) 103 – 105 GPa Elongation at break 28 – 32 % Hardness 120 HB Physical Properties Corrosion resistance Excellent Magnetism Non-magnetic Weldability High Thermal Properties Maximum service temperature 320 – 400 °C Thermal […]
Titanium Grade 2 | 3.7035
Property Value Mechanical Properties Ultimate tensile strength 420 – 470 MPa Yield strength 330 – 360 MPa Young’s modulus (modulus of elasticity) 105 – 110 GPa Elongation at break 23 – 25 % Hardness 80 – 82 HRB Physical Properties Corrosion resistance Excellent Magnetism Non-magnetic Weldability High Thermal Properties Maximum service temperature 320 – 430 […]
Titanium Grade 5 | 3.7164 | Ti6Al4V
Property Value Mechanical Properties Ultimate tensile strength 920 – 1000 MPa Yield strength 830 – 880 MPa Young’s modulus (modulus of elasticity) 113.8 GPa Elongation at break 9 – 11 % Hardness 334 HB Physical Properties Corrosion resistance Very high Magnetism Low Common Applications Aerospace