| Property | Value |
|---|---|
| Mechanical Properties | |
| Ultimate tensile strength | 520 – 560 MPa |
| Yield strength | 460 – 470 MPa |
| Young’s modulus (modulus of elasticity) | 69 – 76 GPa |
| Elongation at break | 6 – 9 % |
| Physical Properties | |
| Corrosion resistance | Moderate |
| Magnetism | Non-magnetic |
| Weldability | Poor |
| Thermal Properties | |
| Maximum service temperature | 100 °C |
| Thermal expansion coefficient | 22.9 – 24.1 × 10-6/ºC |
| Thermal conductivity | 131 – 137 W/(m⋅°C) |
| Electrical Properties | |
| Electrical resistivity | 5.2 μΩ*cm |
| Post Treatments | |
| Post-Processing | Annealing & Cold working |
| Anodizing compatibility | Not recommended – due to the high amount of zinc that the material contains, dark spots or corroded marks may be observed |
| Common Applications | |
| Aircraft and aerospace | Marine |
| Transportation | |