Property | Value |
---|---|
Mechanical Properties | |
Ultimate tensile strength | 30 – 59 MPa |
Yield strength | 9 MPa |
Young’s modulus (modulus of elasticity) | 2.9 – 3.1 GPa |
Elongation at break | 330 – 587 % |
Hardness | 85A – 95A |
Plastic
FDM
Property | Value |
---|---|
Mechanical Properties | |
Ultimate tensile strength | 30 – 59 MPa |
Yield strength | 9 MPa |
Young’s modulus (modulus of elasticity) | 2.9 – 3.1 GPa |
Elongation at break | 330 – 587 % |
Hardness | 85A – 95A |
Aluminum, Alloy Steel
± 0.3% starting from ± 0.3 mm
(0.012 in)
Lead duration: 5 business days
Laser Cutting. Bending, Post-Processing
Tolerances as low as ± 0.04 in (0.1 mm)
Lead duration: 5 business days
Prototypes and production tooling
Wide range of part complexities and sizes
1 to 1M parts
Milling, turning and post-processing
Tolerances down to ±.020 mm (±.001 in)
Lead times from 5 business days
FDM, SLA, SLS, MJF
± 0.3% with a lower limit of ± 0.3 mm (± 0.012 in)
Lead times from 1 business day
Explore the top future of metal fabrication for 2024, including 3D printing, automation, and advanced materials. Discover how
The article under review discusses how 3D metal printing produces metal new techniques with impacts on methods like
Descubra estrategias esenciales para optimizar los procesos de mecanizado CNC y lograr una mayor eficacia y productividad. Explore técnicas de vanguardia, desde la herramienta
Explore cómo la fundición a presión en cámara fría está dando forma al futuro de la fabricación de grandes volúmenes con su precisión, eficiencia y
Explore cómo la fundición a presión en la fabricación aeroespacial con componentes ligeros y de alta resistencia. Conozca el impacto de la fundición a presión en la aeronáutica
Aprenda el proceso de fundición a presión, desde el diseño del molde hasta la inyección de metal, el enfriamiento y la expulsión. Descubra cómo este proceso de alta precisión
Derechos de autor © 2024 MXY Machining
Derechos de autor © 2024 MXY Machining